    Specification Ecarb - Vapor Phase Series 3 x 6 Method
    +3 Mesh (+6.73 mm) 5% Max. 5% Max.       ASTM D2862
    -6 Mesh (-3.35 mm) 5% Max. 5% Max.       ASTM D2862
    Iodine Value (Minimum) 900 950       ASTM D4607
    CTC Value in % (Minimum) 45 50       ASTM D3467
    Apparent Density in Kg/m3 (Minim.) 500 450       ASTM D2854
    Surface Area NA NA        
    Ball Pan Hardness 95% Min. 95% Min.       ASTM D3802
    Moisture 5% Max. 5% Max.       ASTM D2867
    Ash 3% Max. 3% Max.       ASTM D2866
    PH 9 – 11 9 – 11       ASTM D3838
    Specification Ecarb - Vapor Phase Series 4 x 8 Method
    +4 Mesh (+4.75 mm) 5% Max. 5% Max. 5% Max. 5% Max. 5% Max. ASTM D2862
    -8 Mesh (-2.36 mm) 5% Max. 5% Max. 5% Max. 5% Max. 5% Max. ASTM D2862
    Iodine Value (Minimum) 900 Min. 950 Min. 1050 Min. 1100 Min. 1250 Min. ASTM D4607
    CTC Value in % (Minimum) 45 50 55 60 75 ASTM D3467
    Apparent Density in Kg/m3 (Minim.) 510 490 480 460 430 ASTM D2854
    Surface Area NA NA NA NA NA  
    Ball Pan Hardness 98% Min. 98% Min. 98% Min. 98% Min. 95% Min. ASTM D3802
    Moisture 5% Max. 5% Max. 5% Max. 5% Max. 5% Max. ASTM D2867
    Ash 3% Max. 3% Max. 3% Max. 3% Max. 3% Max. ASTM D2866
    PH 9 – 11 9 – 11 9 – 11 9 – 11 9 – 11 ASTM D3838
    Specification Ecarb - Vapor Phase Series 6 x 16 Method
    +6 Mesh (+3.35 mm) 5% Max. 5% Max. 5% Max. 5% Max. 5% Max. ASTM D2862
    -16 Mesh (-1.18 mm) 5% Max. 5% Max. 5% Max. 5% Max. 5% Max. ASTM D2862
    Iodine Value (Minimum) 950 Min. 1000 Min. 1100 Min. 1150 Min. 1300 Min. ASTM D4607
    CTC Value in % (Minimum) 45 50 55 60 75 ASTM D3467
    Apparent Density in Kg/m3 (Minim.) 540 520 520 480 430 ASTM D2854
    Surface Area NA NA NA NA NA  
    Ball Pan Hardness 98% Min. 98% Min. 98% Min. 98% Min. 95% Min. ASTM D3802
    Moisture 5% Max. 5% Max. 5% Max. 5% Max. 5% Max. ASTM D2867
    Ash 3% Max. 3% Max. 3% Max. 3% Max. 3% Max. ASTM D2866
    PH 9 – 11 9 – 11 9 – 11 9 – 11 9 – 11 ASTM D3838